|
optic bundle.jpg|thumb|right|350px|A bundle of optical fibers. Theoretically, using advanced techniques such as DWDM, the modest number of fibers seen here could have sufficient bandwidth to easily carry the sum of all types of current data transmission needs for the entire planet. (~100 terabits per second per fiber http://www.lucent.com/press/0601/010628.bla.html) An optical fiber is a glass or plastic fiber designed to guide light along its length by total internal reflection. Fiber optics is the branch of applied science and engineering concerned with such optical fibers. Optical fibers are widely used in fiber-optic communication, which permits digital data transmission over longer distances and at higher data rates than electronic communication. They are also used to form sensors, and in a variety of other applications. The operating principle of optical fibers applies to a number of variants including multi-mode optical fibers, single-mode optical fibers, graded-index optical fibers, and step-index optical fibers. Because of the physics of the optical fiber, special methods of splicing fibers and of connecting them to other equipment are needed. A variety of methods are used to manufacture optical fibers, and the fibers are also built into different kinds of cables depending on how they will be used. The light-guiding principle behind optical fibers was first demonstrated in Victorian times, but modern optical fibers were only developed beginning in the 1950's. Optical fibers became practical for use in communications in the late 1970's, and since then several technical advances have been made to extend the reach and speed capability of optical fibers, and lower the cost of fiber communications systems. Optical fiber communication The optical fiber can be used as a medium for telecommunication and networking because it is flexible and can be bundled as cables. Although fibers can be made out of transparent plastic, glass, or a combination of the two, the fibers used in long-distance telecommunications applications are always glass, because of the lower optical attenuation. Both multi-mode and single-mode fibers are used in communications, with multi-mode fiber used mostly for short distances (up to 500 m), and single-mode fiber used for longer distance links. Because of the tighter tolerances required to couple light into and between single-mode fibers, single-mode transmitters, receivers, amplifiers and other components are generally more expensive than multi-mode components. Fiber optic sensors Optical fibers can be used as sensors to measure strain, temperature, pressure and other parameters. The small size and the fact that no electrical power is needed at the remote location gives the fiber optic sensor advantages to conventional electrical sensor in certain applications. Optical fibers are used as hydrophones for seismic or SONAR applications. Hydrophone systems with more than 100 sensors per fiber cable have been developed. Hydrophone sensor systems are used by the oil industry as well as a few countries' navies. Both bottom mounted hydrophone arrays and towed streamer systems are in use. The German company Sennheiser developed a microphone working with a laser and optical fibers•. Optical fiber sensors for temperature and pressure have been developed for downhole measurement in oil wells. The fiber optic sensor is well suited for this environment as it is functioning at temperatures too high for semiconductor sensors (Distributed Temperature Sensing). Another use of the optical fiber as a sensor is the optical gyroscope which is in use in the Boeing 767 and in some car models (for navigation purposes) and the use in Hydrogen microsensors. Other uses of optical fibers Fibers are widely used in illumination applications. They are used as light guides in medical and other applications where bright light needs to be brought to bear on a target without a clear line-of-sight path. In some buildings, optical fibers are used to route sunlight from the roof to other parts of the building (see non-imaging optics). Optical fiber illumination is also used for decorative applications, including signs, art, and artificial Christmas trees. Swarovski boutiques use optical fibers to illuminate their crystal showcases from many different angles while only employing one light source. Optical fiber is an intrinsic part of the light-transmitting concrete building product, LiTraCon. Optical fiber is also used in imaging optics. A coherent bundle of fibers is used, sometimes along with lenses, for a long, thin imaging device called an endoscope, which is used to view objects through a small hole. Medical endoscopes are used for minimally invasive exploratory or surgical procedures (endoscopy). Industrial endoscopes (see fiberscope or borescope) are used for inspecting anything hard to reach, such as jet engine interiors. An optical fiber doped with certain rare-earth elements such as erbium can be used as the gain medium of a laser or optical amplifier. Rare-earth doped optical fibers can be used to provide signal amplification by splicing a short section of doped fibre into a regular (undoped) optical fiber line. The doped fiber is optically pumped with a second laser wavelength that is coupled into the line in addition to the signal wave. Both wavelengths of light are transmitted through the doped fiber, which transfers energy from the second pump wavelength to the signal wave. The process that causes the amplification is stimulated emission. Optical fibers doped with a wavelength shifter are used to collect scintillation light in physics experiments. Optical fiber can be used to supply a low level of power (around one watt) to electronics situated in a difficult electrical environment. Examples of this are electronics in high-powered antenna elements and measurement devices used in high voltage transmission equipment. Principle of operation An optical fiber is a cylindrical dielectric waveguide that transmits light along its axis, by the process of total internal reflection. The fiber consists of a core surrounded by a cladding layer. To confine the optical signal in the core, the refractive index of the core must be greater than that of the cladding. The boundary between the core and cladding may either be abrupt, in step-index fiber, or gradual, in graded-index fiber. Multimode fiber
Singlemode fiber
Special-purpose fiber Some special-purpose optical fiber is constructed with a non-cylindrical core and/or cladding layer, usually with an elliptical or rectangular cross-section. These include polarization-maintaining fiber and fiber designed to suppress whispering gallery mode propagation. Materials Glass optical fibers are almost always made from silica, but some other materials, such as fluorozirconate, fluoroaluminate, and chalcogenide glasses are used for longer-wavelength infrared applications. Like other glasses, these glasses have a refractive index of about 1.5. Typically the difference between core and cladding is less than one percent. Plastic optical fiber (POF) is commonly step-index multimode fiber, with core diameter of 1 mm or larger. POF typically has much higher attenuation than glass fiber (that is, the amplitude of the signal in it decreases faster), 1 dB/m or higher, and this high attenuation limits the range of POF-based systems. Fiber fuse At high optical intensities, above 2 megawatts per square centimetre, when a fiber is subjected to a shock or is otherwise suddenly damaged, a fiber fuse can occur. The reflection from the damage vaporizes the fiber immediately before the break, and this new defect remains reflective so that the damage propagates back toward the transmitter at 1–3 meters per second •,•,•. The open fiber control system, which ensures laser eye safety in the event of a broken fiber, can also effectively halt propagation of the fiber fuse •. In situations, such as undersea cables, where high power levels might be used without the need for open fiber control, a "fiber fuse" protection device at the transmitter can break the circuit to prevent any damage. Manufacturing Optical fiber is made by first constructing a large-diameter preform, with a carefully controlled refractive index profile, and then pulling the preform to form the long, thin optical fiber. The preform is commonly made by three chemical vapor deposition methods: inside vapor deposition, outside vapor deposition, and vapor axial deposition. With inside vapor deposition, a hollow glass tube approximately 40 cm in length known as a "preform" is placed horizontally and rotated slowly on a lathe, and gases such as silicon tetrachloride (SiCl4) or germanium tetrachloride (GeCl4) are injected with oxygen in the end of the tube. The gases are then heated by means of an external hydrogen burner, bringing the temperature of the gas up to 1900 kelvins, where the tetrachlorides react with oxygen to produce silica or germania (germanium oxide) particles. When the reaction conditions are chosen to allow this reaction to occur in the gas phase throughout the tube volume, in contrast to earlier techniques where the reaction occurred only on the glass surface, this technique is called modified chemical vapor deposition. The oxide particles then agglomerate to form large particle chains, which subsequently deposit on the walls of the tube as soot. The deposition is due to the large difference in temperature between the gas core and the wall causing the gas to push the particles outwards (this is known as thermophoresis). The torch is then traversed up and down the length of the tube to deposit the material evenly. After the torch has reached the end of the tube, it is then brought back to the beginning of the tube and the deposited particles are then melted to form a solid layer. This process is repeated until a sufficient amount of material has been deposited. For each layer the composition can be varied by varying the gas composition, resulting in precise control of the finished fiber's optical properties. In outside vapor deposition or vapor axial deposition, the glass is formed by flame hydrolysis, a reaction in which silicon tetrachloride and germanium tetrachloride are oxidized by reaction with water (H2O) in an oxyhydrogen flame. In outside vapor deposition the glass is deposited onto a solid rod, which is removed before further processing. In vapor axial deposition, a short seed rod is used, and a porous preform, whose length is not limited by the size of the source rod, is built up on its end. The porous preform is consolidated into a transparent, solid perform by heating to about 1800 kelvins. The preform, however constructed, is then placed in a device known as a drawing tower, where the preform tip is heated and the optic fiber is pulled out as a string. By measuring the resultant fiber width, the tension on the fiber can be controlled to maintain the fiber thickness. This manufacturing process is accomplished by several fiber optic companies, including 3M, Corning Inc., and Molex. In addition, various fiber optic component manufacturers, assembly houses, and custom fiber optic providers exist. Optical fiber cables In practical fibers, the cladding is usually coated with a tough resin ''buffer'' layer, which may be further surrounded by a jacket layer, usually plastic. These layers add strength to the fiber but do not contribute to its optical wave guide properties. For indoor applications, the jacketed fiber is generally enclosed, with a bundle of flexible fibrous polymer (e.g. Kevlar) strength members, in a lightweight plastic cover to form a simple cable. Each end of the cable may be terminated with a specialized optical fiber connector to allow it to be easily connected and disconnected from transmitting and receiving equipment. For use in more strenuous environments, a much more robust cable construction is required. In loose-tube construction the fiber is laid helically into semi-rigid tubes, allowing the cable to stretch without stretching the fiber itself. This protects the fiber from tension during laying and due to temperature changes. Alternatively the fiber may be embedded in a heavy polymer jacket, commonly called "tight buffer" construction. These fiber units are commonly bundled with additional steel strength members, again with a helical twist to allow for stretching. Another critical concern in cabling is to protect the fiber from contamination by water, because its component hydrogen (hydronium) and hydroxyl ions can diffuse into the fiber, reducing the fiber's strength and increasing the optical attenuation. Water is kept out of the cable by use of solid barriers such as copper tubes, water-repellant jelly, or more recently water absorbing powder, surrounding the fiber. Finally, the cable may be armored to protect it from environmental hazards, such as construction work or gnawing animals. Undersea cables are more heavily armored in their near-shore portions to protect them from boat anchors, fishing gear, and even sharks, which may be attracted to the electrical power signals that are carried to power amplifiers or repeaters in the cable. Modern fiber cables can contain up to a thousand fibers in a single cable, so the performance of optical networks easily accommodates even today's demands for bandwidth on a point-to-point basis. However, unused point-to-point potential bandwidth does not translate to operating profits, and it is estimated that no more than 1% of the optical fiber buried in recent years is actually 'lit'. Modern cables come in a wide variety of sheathings and armor, designed for applications such as direct burial in trenches, dual use as power lines , installation in conduit, lashing to aerial telephone poles, submarine installation, or insertion in paved streets. In recent years the cost of small fiber-count pole mounted cables has greatly decreased due to the high Japanese and South Korean demand for Fiber to the Home (FTTH) installations. Termination and splicing
History The history of dielectric optical lightguides goes back to Victorian times, when the total internal reflection principle was used to illuminate streams of water in elaborate public fountains. Later development, in the early-to-mid twentieth century, focused on the development of fiber bundles for image transmission, with the primary application being the medical gastroscope. The first fiber optic semi-flexible gastroscope was patented by Basil Hirschowitz, C. Wilbur Peters, and Lawrence E. Curtiss, researchers at the University of Michigan, in 1956. In the process of developing the gastroscope, Curtiss produced the first glass-clad fibers; previous optical fibers had relied on air or impractical oils and waxes as the low-index cladding material. A variety of other image transmission applications soon followed. In 1965, Charles K. Kao and George A. Hockham of the British company Standard Telephones and Cables were the first to recognize that attenuation of contemporary fibers was caused by impurities, which could be removed, rather than fundamental physical effects such as scattering. They demonstrated that optical fiber could be a practical medium for communication, if the attenuation could be reduced below 20 dB per kilometer (Hecht, 1999, p. 114). By this measure, the first practical optical fiber for communications was invented in 1970 by researchers Robert D. Maurer, Donald Keck, Peter Schultz, and Frank Zimar working for American glass maker Corning Glass Works. They manufactured a fiber with 17 dB optic attenuation per kilometer by doping silica glass with titanium. On 22 April, 1977, General Telephone and Electronics sent the first live telephone traffic through fiber optics, at 6 Mbit/s, in Long Beach, California. The erbium-doped fiber amplifier, which reduced the cost of long-distance fiber systems by eliminating the need for optical-electrical-optical repeaters, was invented by David Payne of the University of Southampton, and Emmanuel Desurvire at Bell Laboratories in 1986. The two pioneers were awarded the Benjamin Franklin Medal in Engineering in 1998. The first transatlantic telephone cable to use optical fiber was TAT-8, based on Desurvire optimized laser amplification technology. It went into operation in 1988. In 1991, the emerging field of photonic crystals led to the development of photonic crystal fiber (Science (2003), vol 299, page 358), which guides light by means of diffraction from a periodic structure, rather than total internal reflection. The first photonic crystal fibers became commercially available in 1996 *. Photonic crystal fibers can be designed to carry higher power than conventional fiber, and their wavelength dependent properties can be manipulated to improve their performance in certain applications. See also Notes | |||||||||||||
|
| ||||||||||||||
 |
|
| |